Polyether Ether Ketone (PEEK) is a high-performance polymer increasingly utilized in additive manufacturing due to its exceptional thermal, chemical, and mechanical properties. Thus, they are used to produce aerospace brackets, fuel system parts, seals, compressor valve plates, etc. This study investigates the mechanical performance of both neat PEEK and glass fiber-reinforced PEEK (PEEK + GF) composites fabricated via fused deposition modeling (FDM). The effects of print speed, print orientation, and post-heat treatment were systematically evaluated. Among the tested orientations, the 0° print direction with post-heat treatment at 250 °C yielded highest tensile strength of ~80 MPa, outperforming the 45° and 90° orientations. Print speeds ranging from 5 to 20 mm/s and annealing temperatures between 250 °C and 300 °C significantly influenced material properties. For neat PEEK, both tensile strength and microhardness improved with increasing print speed and post-heat treatment, peaking at 20 mm/s and 250 °C. However, annealing at 300 °C led to performance degradation, attributing to gas-induced porosity within the material. The PEEK + GF composites achieved a maximum ultimate tensile strength (UTS) of approximately 83 MPa under the same optimal conditions (20 mm/s print speed and 250 °C post-treatment). This enhancement is attributed to improved fiber alignment along the print path, increased crystallinity, and superior interfacial bonding. Notably, the composites did not exhibit the microstructural damage observed in neat PEEK at the higher annealing temperature.
Puli et al. (Mon,) studied this question.