Adjusted Preferential Adsorption of Intermediates via Regulation of the Electronic Structure during the Electrocatalytic CO2 Reduction Process

The surface electronic structures of catalysts play a crucial role in CO2 adsorption and activation. Here, sulfur vacancies are introduced into CuInS2 nanosheets (Vs-CuInS2) to evaluate the effect of electronic structures at the surface-active sites on the electrochemical CO2 reduction reaction (CO2RR). Vs-CuInS2 exhibits a significant disparity in the highest FEformate/FECO (6.50) compared to that of CuInS2 (1.86). Specifically, the maximum current density (Jmax) of carbon products on Vs-CuInS2 is 78.78 mA cm-2, and a Faraday efficiency of carbon products (FEcarbon products) of ≥80% is achieved in 600 mV wide potential windows. In situ Raman measurements and density functional theory calculations elucidate the origin of the apparent alterations in the carbon product selectivity. The introduction of sulfur vacancies realizes the controllable regulation of the local electronic density around the metal active sites, inducing the transformation of *COOH and *OCHO from competitive adsorption on CuInS2 to specific adsorption on Vs-CuInS2. In addition, the regulation of electronic structures on Vs-CuInS2 inhibits *H adsorption. This work reveals the transfer of adsorption of CO2RR intermediates via regulation of the electronic structure, complementing the understanding of the mechanism for the enhanced CO2RR.