This study developed poly(lactic acid) (PLA) biocomposites reinforced with pine wood flour (10, 20, and 30 wt%) to achieve the interphase through chemical modification. Specifically, the wood flour was treated with poly(propylene glycol) toluene 2,4-diisocyanate terminated (PEGTDI), while 1 wt% poly(lactic acid)-g-maleic anhydride (PLA-g-MA) was integrated as a reactive compatibilizer during extrusion and thermocompression. Fourier-transform infrared spectroscopy (FTIR) analysis corroborated the occurrence of urethane formation and ester/anhydride linkages, as substantiated by the presence of characteristic bands indicative of surface carbamation at 1645 and 1726 cm−1. Thermal analysis revealed that both the pine wood flour and coupling agents promoted PLA crystallization; however, thermogravimetric analysis (TGA) indicated a decrease in thermal stability for functionalized composites, suggesting a trade-off between enhanced interfacial interaction and heat resistance. Mechanical testing demonstrated a significant reinforcement effect, with the Young’s modulus increasing by up to 22% in untreated composites. The coupling agents effectively optimized stress transfer at low fiber loadings (10 wt%), while flexural modulus improvements were predominant at higher loadings (20–30 wt%) regardless of treatment. These findings underscore the criticality of surface modification and compatibilizer selection for tailoring the structural and thermo-mechanical properties of PLA-based biocomposites, thereby providing a pathway for optimized performance in structural applications.
Jacobo et al. (Tue,) studied this question.