The evolution of the Li-ion displacements in the 3D interstitial pathways of the cubic garnet-type Li(7)La(3)Zr(2)O(12), cubic Li(7)La(3)Zr(2)O(12), was investigated with high-temperature neutron diffraction (HTND) from RT to 600 °C; the maximum-entropy method (MEM) was applied to estimate the Li nuclear-density distribution. Temperature-driven Li displacements were observed; the displacements indicate that the conduction pathways in the garnet framework are restricted to diffusion through the tetrahedral sites of the interstitial space.