This study develops a ternary Fe-based geopolymer system composed of metakaolin (MK), red mud (RM), and fly ash (FA) for the preparation of sustainable water-retaining subgrade materials for sponge-city roadbed applications. Unlike conventional formulations primarily designed for structural strength or rapid permeability, the proposed MK–FA–RM system was designed to improve water-storage capacity while maintaining adequate mechanical support and environmental compatibility. In this ternary system, MK provides highly reactive aluminosilicate species for geopolymer network formation, RM introduces Fe-bearing phases and enhances industrial solid-waste utilization, and FA contributes to particle packing, workability, and resource efficiency. A constrained ternary mixture design implemented using Design-Expert software was adopted to optimize precursor proportions. Within the investigated compositional range, the fitted first-order mixture model showed acceptable statistical adequacy for preliminary composition screening (R2 = 0.86). The optimal blend (60% MK, 30% RM, and 10% FA) achieved a 7-day compressive strength of 8.37 MPa and a water retention rate of 35.3% under ambient curing conditions, satisfying the strength requirement considered for the target subgrade/base-layer application. Microstructural and phase analyses suggest that the synergistic interaction of the three precursors promoted Fe-modified aluminosilicate gel formation together with conventional geopolymer gel products, while improving matrix continuity and preserving interconnected pore space for water storage. This multiscale structural effect helps explain how the material achieved a balance between water retention capacity and mechanical support. Under the tested conditions, the material maintained acceptable residual strength after short-term exposure to water, acid, and sulfate-containing solutions. Life-cycle assessment indicated a 70% reduction in CO2 emissions compared with ordinary Portland cement, while pilot-scale cost analysis showed a 39% lower production cost than MetaMax-based geopolymer materials. Pilot-scale application further demonstrated the constructability and water-regulation potential of the material in practical environments. Overall, the proposed ternary Fe-based geopolymer demonstrates that Fe-rich industrial wastes can be engineered into low-carbon and economically viable water-retaining subgrade materials that balance hydraulic regulation, structural adequacy, and sustainability. Nevertheless, long-term durability, cyclic loading performance, and direct nanoscale characterization of Fe-bearing gel evolution still require further investigation.
Wu et al. (Fri,) studied this question.