Sub-10 nm Graphene Nanoribbon Arrays are fabricated over large areas by etching CVD-grown graphene. A mask is used made by the directed self-assembly of a cylindrical PS-b-PDMS block copolymer under solvent annealing guided by a removable template. The optimized solvent annealing process, surface-modified removable polymeric templates, and high Flory-Huggins interaction parameters of the block copolymer enable a highly aligned array of nanoribbons with low line edge roughness to be formed. This leads to a higher on/off ratio and stronger temperature dependence of the current for nanoribbon FETs, and a photocurrent which is 30 times larger compared to unpatterned graphene. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.
Son et al. (Tue,) studied this question.