Nickel-iron (oxy)hydroxide (NiFeOxHy) stands as a cutting-edge nonprecious electrocatalyst for the oxygen evolution reaction (OER). However, the intrinsic thermodynamic instability of nickel and iron as anode materials in pure water-fed electrolyzers poses a significant durability challenge. In this study, an anion exchange ionomer coating was applied to NiFeOxHy to modify the local pH between a membrane and an electrode. This effectively extended the diffusion length of hydroxide anions toward the electrode, establishing an alkaline local pH environment. Stability tests with the ionomer coating showed reduced Ni dissolution. Moreover, locally resolved current density measurements were used to demonstrate a notably lower degradation rate during stability testing, revealing a 6-fold increase in stability with the ionomer on NiFeOxHy. In situ Raman spectroscopy in a neutral pH electrolyte confirmed inhibited Ni oxidation with the ionomer, mitigating Ni dissolution and enhancing stability of state-of-the-art NiFeOxHy catalysts in pure water-fed water electrolyzers.
Kang et al. (Tue,) studied this question.