This study addresses a persistent challenge in polymer joining: the laser welding of two incompatible thermoplastics, polypropylene (PP) and high-density polyethylene (HDPE). The key innovation lies in modifying HDPE with 3 wt% graphene nanoplatelets (GNPs) via material extrusion (MEX), which raises its melting temperature from 136.8 °C to 138.8 °C and increases crystallinity from 46.9% to 51.4%, as confirmed by differential scanning calorimetry (DSC). This thermal adjustment brings HDPE closer to PP’s melting behavior, enabling effective laser butt welding using a pulsed CO2 laser. A Box–Behnken design within response surface methodology (RSM) was employed to model the individual and interactive effects of laser power (30–50 W), welding speed (15–25 mm/s), and pulse frequency (25–35 Hz) on the flexural and impact strength of the welded joints. Scanning electron microscopy (SEM) revealed that optimal welding conditions—laser power of 49 W, welding speed of 20 mm/s, and pulse frequency of 35 Hz—produce a defect-free interface with complete polymer chain interdiffusion. Under these optimized conditions, the regression models predicted a flexural strength of 69.7 MPa and an impact strength of 21.9 kJ/m2. Confirmation experiments yielded 68.2 MPa and 22.6 kJ/m2, with relative errors below 4%, validating the predictive capability of the models. This work demonstrates that GNP-mediated thermal property modification, coupled with statistical process optimization, offers a viable pathway for manufacturing high-performance dissimilar polymer joints for lightweight structural applications.
Maged F. Alotaibi (Thu,) studied this question.