Metal Matrix Composites (MMCs) have evoked a keen interest in recent times for potential applications in aerospace and automotive industries owing to their superior strength to weight ratio and high temperature resistance. The widespread adoption of particulate metal matrix composites for engineering applications has been hindered by the high cost of producing components. Although several technical challenges exist with casting technology yet it can be used to overcome this problem. Achieving a uniform distribution of reinforcement within the matrix is one such challenge, which affects directly on the properties and quality of composite material. In the present study a modest attempt has been made to develop aluminium based silicon carbide particulate MMCs with an objective to develop a conventional low cost method of producing MMCs and to obtain homogenous dispersion of ceramic material. To achieve these objectives two step-mixing method of stir casting technique has been adopted and subsequent property analysis has been made. has been chosen as matrix and reinforcement material respectively. Experiments have been conducted by varying weight fraction of SiC (5%, 10%, 15%, 20%, 25%, and 30%), while keeping all other parameters constant. The results indicated that the 'developed method' is quite successful to obtain uniform dispersion of reinforcement in the matrix. An increasing trend of hardness and impact strength with increase in weight percentage of SiC has been observed. The best results (maximum hardness 45.5 BHN & maximum impact strength of 36 N-m.) have been obtained at 25% weight fraction of SiC. The results were further justified by comparing with other investigators.
Singla et al. (Thu,) studied this question.