Time-resolved photoluminescence measurements reveal a minority carrier lifetime of 412 ns at 77 K under low excitation for a long-wavelength infrared InAs/InAs0.72Sb0.28 type-II superlattice (T2SL). This lifetime represents an order-of-magnitude increase in the minority carrier lifetime over previously reported lifetimes in long-wavelength infrared InAs/Ga1−xInxSb T2SLs. The considerably longer lifetime is attributed to a reduction of non-radiative recombination centers with the removal of Ga from the superlattice structure. This lifetime improvement may enable background limited T2SL long-wavelength infrared photodetectors at higher operating temperatures.