Application of dynamic mechanical analysis for the study of the interfacial region in carbon fiber/epoxy composite materials

Abstract The application of dynamic mechanical analysis (DMA) for quantifying interfacial interactions in composites is briefly reviewed. Carbon fiber/epoxy composites with fiber volume fractions of 12, 17, 38 and 61 vol% were subjected to flexural deformation on a Dupont DMA 983 instrument. The dependencies of dynamic mechanical properties of the composites on experimental parameters such as oscillation mode, amplitude, frequency, and temperature were investigate. As opposed to the storage modulus, the loss modulus is found to be sensitive to all parameters. In a fixed multiple frequency mode, the loss modulus of the composites increases with oscillation amplitude and decreases with frequency and the number of tests. The information produced in the resonant mode is more reproducible. An additional damping at the interfaces, apart from those of the constituents, suggests a poor interface adhesion in these composites. A linear relationship between the excess damping at the interfaces and the fiber volume fraction shows a similar interface quality for these composites having different fiber volume fractions. The detection of interfacial properities was found to be more sensitive in the flexural deformation mode than in the torsional mode. At temperatures higher than the glass transition temperature of the matrix, the effective volume fraction of the matrix is reduced. Such a reduction can be interpreted from the mismatch of thermal expansion of the matrix and the fibers.