In, Ga, and Se were coevaporated to form precursor films of (Inx,Ga1−x)2Se3. The precursors were then converted to CuInxGa1−xSe2 by exposure to a flux of Cu and Se. The final films were smooth, with tightly packed grains, and had a graded Ga content as a function of film depth. Photovoltaic devices made from these films showed good tolerance in device efficiency to variations in film composition. A device made from these films resulted in the highest total-area efficiency measured for any non-single-crystal, thin-film solar cell, at 15.9%.