Controlled Growth of Large-Area, Uniform, Vertically Aligned Arrays of α-Fe2O3 Nanobelts and Nanowires

Vertically aligned iron oxide nanobelt and nanowire arrays have been synthesized on a large-area surface by direct thermal oxidation of iron substrates under the flow of O(2). The effects of reactive gas pressure, composition, and temperature have been systematically studied. It was found that nanobelts (width, tens of nanometers; thickness, a few nanometers) are produced in the low-temperature region (approximately 700 degrees C) whereas cylindrical nanowires tens of nanometers thick are formed at relatively higher temperatures (approximately 800 degrees C). Both nanobelts and nanowires are mostly bicrystallites with a length of tens of micrometers which grow uniquely along the 110 direction. The growth habits of the nanobelts and nanowires in the two temperature regions indicate the role of growth rate anisotropy and surface energy in dictating the ultimate nanomorphologies.