There's more to LiFe: When used as an electrode in a lithium half cell, the metal–organic framework LixFeIIxFeIII1−x (OH) 0. 8F0. 2L (L=O2CC6H4CO2) shows a reversible redox process around 3. 0 V versus Li+/Li0 with interesting capacity retention and rate capability (see voltage profile for a LixFe (OH) 0. 8F0. 2L half cell; inset: representation of lithium insertion upon oxidation to Li+). Supporting information for this article is available on the WWW under http: //www. wiley-vch. de/contents/jc₂002/2007/z605163ₛ. pdf or from the author. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.