Characterization of bulk to thin wall mechanical response transition in powder bed AM

Purpose In the development of powder bed additive manufacturing (AM) process parameters, the characterization of mechanical properties is generally performed through relatively large mechanical test samples that represent a bulk response. This provides an accurate representation of mechanical properties for equivalently sized or larger parts. However, as feature size is reduced, mechanical properties transition from a standard bulk response to a thin wall response where lower power border scans and surface roughness have a larger effect. Design/methodology/approach For this study, samples of wall thickness varying between 4.0 and 0.25 mm were built in 304L on the selective laser melting (SLM) platform and Ti-6Al-4V on the electron beam melting (EBM) platform. Samples were then mechanically tested, and fractography was performed for analysis. Findings This study experimentally identifies the threshold between bulk and thin wall mechanical properties for 304L SS on the SLM platform and Ti-6Al-4V on the EBM platform. A possible method for improving those properties and shifting the transition from bulk to thin wall response to smaller wall thicknesses by manipulation of scan pattern was investigated. Originality/value This study is a novel investigation into the effect of reduced wall thickness on the mechanical properties of a part produced by powder bed AM.