The research field on perovskite solar cells (PSCs) is seeing frequent record breaking in the power conversion efficiency (PCE). However, organic-inorganic hybrid halide perovskites and organic additives in common hole-transport materials (HTMs) exhibit poor stability against moisture and heat. Here we report the successful fabrication of all-inorganic PSCs without any labile or expensive organic components. The entire fabrication process can be operated in ambient environment without humidity control (e.g., a glovebox). Even without encapsulation, the all-inorganic PSCs present no performance degradation in humid air (90-95% relative humidity, 25 °C) for over 3 months (2640 h) and can endure extreme temperatures (100 and -22 °C). Moreover, by elimination of expensive HTMs and noble-metal electrodes, the cost was significantly reduced. The highest PCE of the first-generation all-inorganic PSCs reached 6.7%. This study opens the door for next-generation PSCs with long-term stability under harsh conditions, making practical application of PSCs a real possibility.
Liang et al. (Sat,) studied this question.