Inspired by natural mineralization processes, here we present the stepwise mineralization of hydrogels with synthetic control over the amount of deposited CaP i and selective tuning of the coating composition. Alternate immersion of the hydrogel at 3 min intervals in calcium salt (Ca 2+ ) and inorganic phosphate (P i ) solutions under mild aqueous conditions results in the layer-by-layer deposition of a precursor CaP i polymorph, dicalcium phosphate dihydrate (DCPD, Ca/P i 1.12 ± 0.07), as a surface coating. Successive immersion cycles were shown to linearly increase the amount of deposited Ca 2+ and P i ions over 20 cycles enabling direct control over the mineral coating density and crystal morphology. Conversion of the DCPD coating to apatite (CaP i 1.61 ± 0.02) is induced by aqueous hydrolysis at physiological temperature and pH (7.4, 37 °C, 5 days). After conversion, the apatite coating density was found to correlate with the amount of mineral initially deposited as DCPD, indicating this approach to mineralization imparts simultaneous synthetic control over the coating composition and density on the hydrogel substrate. Mineralized coatings were characterized by XRD, ATR-IR spectroscopy, SEM-EDX, and quantitative analysis of Ca 2+ and P i ions. Supplementation of the conversion solution with Ca 2+, P i, SBF, F –, or citrate ions results in apatite coatings exhibiting variations in chemical composition and morphology. In the presence of added Ca 2+ ions and SBF, an increase in Ca 2+ content of the coating is observed, and the resulting particles exhibit growth as plates and petal like clusters, respectively. Conversion with F – ions results in the formation of spherical F-apatite particles that exhibit clearly resolved peaks in the XRD pattern. Citrate ions were found to restrict the growth of apatite particles. The described deposition-conversion approach overcomes longstanding limitations in CaP i -based biomaterials as a versatile method for the predictable and tunable synthesis of CaP i coatings of preformed biopolymer substrates.
Harding et al. (Thu,) studied this question.