Understanding the Low-Voltage Hysteresis of Anionic Redox in Na2Mn3O7

The large-voltage hysteresis remains one of the biggest barriers to optimizing Li/Na-ion cathodes using lattice anionic redox reaction, despite their very high energy density and relative low cost. Very recently, a layered sodium cathode Na2Mn3O7 (or Na4/7Mn6/71/7O2, is vacancy) was reported to have reversible lattice oxygen redox with much suppressed voltage hysteresis. Yet, the structural and electronic structural origin of this small-voltage hysteresis has not been well understood. In this article, through systematic studies using ex situ/in situ electron paramagnetic resonance and X-ray diffraction, we demonstrate that the exceptional small-voltage hysteresis (+ ions from distorted octahedral sites, while the 4. 5 V plateau is linked to a reversible shrink/expansion process of the manganese-site vacancy during (de) intercalation of Na+ ions at distorted prismatic sites. It is expected that these findings will inspire further exploration of new cathode materials that can achieve both high energy density and efficiency by using lattice anionic redox.