Structure Tuning, Strong Second Harmonic Generation Response, and High Optical Stability of the Polar Semiconductors Na1–xKxAsQ2

The mixed cation compounds Na1–xKxAsSe2 (x = 0.8, 0.65, 0.5) and Na0.1K0.9AsS2 crystallize in the polar noncentrosymmetric space group Cc. The AAsQ2 (A = alkali metals, Q = S, Se) family features one-dimensional (1D) 1/∞AQ2– chains comprising corner-sharing pyramidal AQ3 units in which the packing of these chains is dependent on the alkali metals. The parallel 1/∞AQ2– chains interact via short As···Se contacts, which increase in length when the fraction of K atoms is increased. The increase in the As···Se interchain distance increases the band gap from 1.75 eV in γ-NaAsSe2 to 2.01 eV in Na0.35K0.65AsSe2, 2.07 eV in Na0.2K0.8AsSe2, and 2.18 eV in Na0.1K0.9AsS2. The Na1–xKxAsSe2 (x = 0.8, 0.65) compounds melt congruently at approximately 316 °C. Wavelength-dependent second harmonic generation (SHG) measurements on powder samples of Na1–xKxAsSe2 (x = 0.8, 0.65, 0.5) and Na0.1K0.9AsS2 suggest that Na0.2K0.8AsSe2 and Na0.1K0.9AsS2 have the highest SHG response and exhibit significantly higher laser-induced damage thresholds (LIDTs). Theoretical SHG calculations on Na0.5K0.5AsSe2 confirm its SHG response with the highest value of d33 = 22.5 pm/V (χ333(2) = 45.0 pm/V). The effective nonlinearity for a randomly oriented powder is calculated to be deff = 18.9 pm/V (χeff(2) = 37.8 pm/V), which is consistent with the experimentally obtained value of deff = 16.5 pm/V (χeff(2) = 33.0 pm/V). Three-photon absorption is the dominant mechanism for the optical breakdown of the compounds under intense excitation at 1580 nm, with Na0.2K0.8AsSe2 exhibiting the highest stability.