Abstract Gas diffusion electrodes (GDE) obtained by sputtering metal films on polytetrafluoroethylene (PTFE) membranes are among the most performant electrodes used to electrochemically reduce CO 2 . The present work reveals several essential aspects for fabricating performant PTFE‐based gas diffusion electrodes (GDEs) for CO 2 electroreduction (CO 2 R). We show that adding an additive layer (a mixture of carbon and Nafion™ or Nafion™ only) is required for stabilizing the metal catalyst film (Cu), deposited via sputtering on the PTFE membrane, during the CO 2 R experiments. We found that the PTFE membrane thickness used in the GDE fabrication plays an essential role in electrode performance. The quantification of the products formed during the CO 2 R conducted in a flow‐cell electrolyzer revealed that on thinner membranes, CO 2 R is the dominant process while on thicker ones, the H 2 formation is promoted. Thus, the PTFE membrane influences the CO 2 transport to the catalyst layer and can be used to promote the CO 2 R while maintaining a minimum H 2 production.
Huq et al. (Thu,) studied this question.