This work demonstrates vertical -Ga2O3 Schottky barrier diodes (SBDs) breaking through the power figure of merit of 1 GW/cm2 without edge termination. The unreliable surface on the top of 1. 2 10 ^{16} cm−3 drift region, which naturally formed in air, was removed by inductively coupled plasma etching. The repaired surface was exposed to ambient air for less than 10 minutes during the entire preparation process. Compared with the excessive air exposure samples, the leakage current was well suppressed for the Ni/ -Ga2O3 SBDs fabricated on a clean surface. Moreover, the blocking voltage reaches a maximum value of 1720 V, and the forward/reverse characteristics of the diodes on the same wafer show good uniformity. These results pave the way for further improving the performance of -Ga2O3 devices and verify the potential of -Ga2O3 SBDs for power applications.