Surface modification of yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) using lasers for adhesion enhancement with resin-matrix cement has been increasingly explored. However, Y-TZP is chemically inert and non-reactive, demanding surface modification using alternative approaches to enhance its bond strength to resin-matrix cements. The main aim of this study was to conduct an integrative review on the influence of ultrashort pulse laser patterning of zirconia (3Y-TZP) for enhanced bonding to resin-matrix cements. An electronic search was performed on web of science, SCOPUS, Pubmed/Medline, Google Scholar and EMBASE using a combination of the following search items: zirconia, 3Y-TZP, surface modification, laser surface treatment, AND laser, ultrashortpulse laser, bonding, adhesion, and resin cement. Articles published in the English language, up to January 2022, were included regarding the influence of surface patterning on bond strength of Y-TZP to resin-matrix cements. Out of the 12 studies selected for the present review 10 studies assessed femtosecond lasers while 2 studies assessed picosecond lasers. Ultrashort pulsed laser surface patterning successfully produced different surface morphological aspects without damaging the bulk properties of zirconia. Contrarily, defects such as micro-cracks occurs after surface modification using traditional methods such as grit-blasting or long-pulsed laser patterning. Ultrashort pulsed laser surface patterning increase bond strength of zirconia to resin-matrix cements and therefore such alternative physical method should be considered in dentistry. Also, surface defects were avoided using ultrashort pulsed laser surface patterning, which become the major advantage when compared with traditional physical methods or long pulse laser patterning.
Sahoo et al. (Mon,) studied this question.