The common, commercial reversible thermochromic (RT) melamine–formaldehyde resin microcapsules containing formaldehyde are very harmful to human health. To address this issue, we successfully prepared a novel formaldehyde-free microcapsule via interfacial polymerization using RT compositions as the core and poly(urethane-urea) (PUU) as the shell. The core material consisted of a color former (crystal violet lactone), a developer (bisphenol AF), and a solvent (methyl stearate). To optimize the synthesis of the microcapsules, an L9 (34) orthogonal design and single-factor experiments were employed to analyze the effects of four factors (N3300-to-L75 shell material mass ratio, core-to-shell material mass ratio, emulsifier concentration, and shear rate during emulsification) on the encapsulation efficiency. The results showed that the optimal parameter values were as follows: a shear rate of 2500 rpm, N3300-to-L75 shell material mass ratio of 1:4, core-to-shell material mass ratio of 11:5, and emulsifier concentration of 3.5%. The influence of the shear rate on the particle size and distribution, surface morphology, dispersibility, and reversible thermochromic properties of the microcapsules was investigated. Furthermore, analyses on the phase-change characteristics, thermal stability, ultraviolet aging, and solvent and acid–base resistances of the microcapsules were conducted systematically. Finally, a reversible thermochromic mark containing the RTPUU microcapsules was designed and fabricated, which could be used against falsification. Moreover, these RTPUU microcapsules can be potentially used for anticounterfeiting applications.
Liu et al. (2023) studied this question.