Evaluation of Bond Strength of Three Glass Fiber Post-systems Cemented to Large Root Canals

SUMMARY The aim of this study was to evaluate the push-out bond strength and the failure mode of single adjustable posts (SPLENDOR SAP), anatomical posts (AP), or computer-aided design/computer-aided manufacturing (CAD-CAM) posts cemented to flared root canal dentin with self-adhesive dual-cure resin cement. Thirty single-rooted premolars received endodontic treatment with gutta-percha and a calcium hydroxide–based endodontic cement. After 24 hours, the canal spaces were enlarged with burs. The tooth specimens were divided equally into three groups (n=10), according to the glass fiber post (GFP) system: AP—prefabricated GFP (Reforpost #2, Angelus) was relined with composite resin (Filtek Z350 XT, 3M ESPE); SPLENDOR SAP—GFP was used with a glass fiber sleeve to adjust the adaptation (Splendor SAP, Angelus); and CAD-CAM—a resin pattern was obtained and scanned to produce a CAD-CAM GFP (Fiber CAD Lab, Angelus) milled using a subtractive technique. The three GFP systems were cemented with self-adhesive resin cement (Rely X U200, 3M ESPE). The roots were fixed to an acrylic resin plate used to section them into specimens of cervical, middle, and apical thirds. Then, the slices were attached to a universal testing machine to perform the push- out test at a speed of 0.5 mm/min and a load of 50 Kgf. The posttest specimens were examined under a stereoscopic microscope to evaluate the failure mode. The bond strength variable was analyzed using a generalized linear model, following a split-plot design. Failure mode analysis was performed using Fisher exact test. The significance level adopted was 5%. There was no significant difference among the GFP systems or among the thirds, in terms of bond strength (p0.05), nor was there any significant association between the systems and the failure mode (p0.05). Most specimens presented mixed or adhesive failure between resin cement and dentin. It was concluded that the bond strength to flared root dentin was not influenced by the GFP system or the root third.