Casting, as a fundamental process in metal forming, finds widespread applications in the manufacturing industry. The advent of 3D printing hollow sand mold technology presents a novel method for casting technology to revolutionize traditional dense sand molds, offering increased flexibility in achieving quality control and improvement in casting processes. Consequently, this study delves into an examination of the mechanical strengths of 3D-printed sand molds with complex hollow structures and further investigates the influence of hollow sand mold concession on castings. The results indicate that compressive and high-temperature residual tensile and bending strengths vary in hollow structures. Multi-layer shells have greater high-temperature residual tensile, compressive, and bending strengths than truss hollow sand molds with roughly the same hollow volume fraction. Compared to dense sand molds, hollow sand molds, which have a lower mechanical strength, have better retractability, which helps reduce the residual stress and crack tendency of castings. The breaking of hollow structures is limited to local areas, unlike the penetrative cracking of dense sand molds. The I-beam-shaped casting test results indicate that a hollow structure is beneficial for the preservation of the integrity of a sand mold during the casting process. Compared to dense and truss hollow molds, a multi-layer shell hollow sand structure has the comprehensive advantages that it improves retractability while maintaining strength relatively well, reduces the residual stress, and avoids cracks in castings and itself.
Xu et al. (Wed,) studied this question.