We examined how different methods of surface treatment and different universal adhesives with or without extra silane affected the repair bonding strength of hybrid ceramic CAD/CAM restorations. Cerasmart specimens (n=320) were subjected to thermocycling and assigned to the following surface pretreatment protocols: control, diamond bur (DB), hydrofluoric acid (HF), and tribochemical silica coating (TSC). Half the specimens received a coating of silane, followed by application of the universal adhesives Futurabond M+ (FMU), Tokuyama Universal Bond (TUB), Single Bond Universal (SBU), or Clearfil Universal Bond Quick (CUQ) (n=10). A hybrid composite resin was used to simulate repair; then the specimens underwent further thermocycling. Shear bond strength (SBS) was determined and modes of failure were examined. The TSC-CUQ silane (−) group showed the highest SBS values. The best repairs were obtained when the surface was treated with TSC, with the exception of the DB-TUB silane (−) group. TUB increased SBS more than the other adhesives. Additional silane decreased SBS in the HF-TUB and TSC-CUQ groups, while increasing it in the TSC-TUB and DB-FMU groups (p<0.05).
DOĞAN et al. (Thu,) studied this question.