Stiffness Retention in Cyclic-Loaded CFRP Composites Produced via Novel Automatic Tape Laying

Sixteen-head automatic tape laying of non-crimped carbon-fibre-reinforced plastic is performed, and the fibre alignment is compared with that produced via hand laying. The effect of fibre alignment is tested via quasi-static and cyclic three-point bending tests. Using the Fill Multilayer (a 16-head tape-laying machine), precision fibre laying of unidirectional fabrics is performed with deliberate misalignment to examine the effect of fibre orientation and investigate the random effect on longitudinal misalignment. The automatic tape-layered coupons are compared with hand-layered carbon fibre tapes to investigate the relationship between the fibre alignment and the flexural strength. A 52% reduction in the fibre alignment scatter is achieved via the Fill Multilayer. Fibre orientation increases lead to a higher flexural strength of 16.08% for Fill Multilayer-made coupons compared with hand-layered samples. An investigation of the correlation between fibre alignment and flexural strength shows that shear-based failure increases exponentially as the alignment decreases. Fill Multilayer-made coupons have a higher void concentration due to ultrasonic welding, but also the highest modulus and flexural strength, as fibre misalignment is reduced to 1.68°, with a modulus degradation of 1.4%.