Crystal Structures and Superconducting Properties of Metallic Double-Chain Based Cuprate Pr2Ba4Cu7O15−δ

We demonstrated the lattice structures and the superconducting phases of metallic double-chain based cuprate Pr2Ba4Cu7O15−δ exhibiting higher Tc. After the oxygen heat treatment on citrate pyrolysis precursors, their reduction treatment followed by a quench procedure caused higher Tc samples with 26. 5–30 K. The crystal structural parameters for the superconducting sample (δ = 0. 81) were analyzed from the powder synchrotron X-ray diffraction data using RIETAN-FP program. The effect of magnetic field on the superconducting phase of these samples with different oxygen defects (δ = 0. 73, 0. 81, and 0. 87) was examined, for our understanding of the superconducting magnetic field–temperature phase diagram. For the δ = 0. 87 sample with Tc ∼ 30 K, the resistive critical field \ (H₂^*\) was estimated to be 13 T at 4. 2 K. The oxygen deficiency dependence on Tc, on for our samples was compared with the data of several other groups.