The microencapsulation of α-tocopherol based on the complex coacervation of low-molecular-weight chitosan (LMWC) and sodium lauryl ether sulphate (SLES) without harmful crosslinkers can provide biocompatible carriers that protect it from photodegradation and air oxidation. In this study, the influence of the microcapsule wall composition on carrier performance, compatibility with a high-water-content vehicle for topical application, and release of α-tocopherol were investigated. Although the absence of aldehyde crosslinkers decreased the encapsulation efficiency of α-tocopherol (~70%), the variation in the LMWC/SLES mass ratio (2:1 or 1:1) had no significant effect on the moisture content and microcapsule size. The prepared microcapsule-loaded carbomer hydrogels were soft semisolids with pseudoplastic flow behavior. The integrity of microcapsules embedded in the hydrogel was confirmed by light microscopy. The microcapsules reduced the pH, apparent viscosity, and hysteresis area of the hydrogels, while increasing their spreading ability on a flat inert surface and dispersion rate in artificial sweat. The in vitro release of α-tocopherol from crosslinker-free microcapsule-loaded hydrogels was diffusion-controlled. The release profile was influenced by the LMWC/SLES mass ratio, apparent viscosity, type of synthetic membrane, and acceptor medium composition. Better data quality for the model-independent analysis was achieved when a cellulose nitrate membrane and ethyl alcohol 60% w/w as acceptor medium were used.
Đekić et al. (Tue,) studied this question.