Impacts of vacancy complexes on the room-temperature photoluminescence lifetimes of state-of-the-art GaN substrates, epitaxial layers, and Mg-implanted layers

For rooting the development of GaN-based optoelectronic devices, understanding the roles of midgap recombination centers (MGRCs), namely, nonradiative recombination centers and deep-state radiative recombination centers, on the carrier recombination dynamics is an essential task. By using the combination of time-resolved photoluminescence and positron annihilation spectroscopy (PAS) measurements, the origins of major MGRCs in the state-of-the-art GaN epilayers, bulk crystals, and Mg-implanted layers were identified, and their concentrations were quantified for deriving the capture coefficients of minority carriers. In this article, potential standardization of the room-temperature photoluminescence lifetime for the near-band-edge emission (τPLRT) as the concentration of major MGRCs well below the detection limit of PAS is proposed. For n-GaN substrates and epilayers grown from the vapor phase, τPLRT was limited by the concentration of carbon on N sites or divacancies comprising a Ga vacancy (VGa) and a N vacancy (VN), VGaVN, when carbon concentration was higher or lower, respectively, than approximately 1016 cm−3. Here, carbon and VGaVN act as major deep-state radiative and nonradiative recombination centers, respectively, while major MGRCs in bulk GaN crystals were identified as VGa(VN)3 vacancy clusters in Na-flux GaN and VGa or VGaVN buried by a hydrogen and/or VGa decorated with oxygen on N sites, VGa(ON)3–4, in ammonothermal GaN. The values of τPLRT in n-GaN samples are compared with those of p-GaN, in which τPLRT was limited by the concentration of VGa(VN)2 in Mg-doped epilayers and by the concentrations of VGaVN and (VGaVN)3 in Mg-implanted GaN right after the implantation and after appropriate activation annealing, respectively.