Heat Treatment of Calcite to Enhance Its Removal of Color Dye Alizarin Red S

The use of color dyes in modern society presents a great challenge to the environment. Thus, extensive studies have been conducted in the last 30 years on the removal of color dyes from aqueous solutions such industrial wastewater. In this study, the removal of alizarin red S (ARS), an anionic dye, from solution by raw calcite (Cal) and heat-treated calcite (HCal) was conducted and compared under different physico-chemical conditions. Based on the isotherm study, the ARS removal capacities increased from 167 to 251 mmol/kg after the Cal was heated to 1000 °C for 3 h. The X-ray diffraction analyses showed no difference in the calcite phase between Cal and HCal after ARS sorption. Fourier-transform infrared results also showed no change in the calcite phase after ARS sorption, except a slightly increase in wavenumber from 713 to 727 cm−1 for the OCO bending of HCal at high ARS sorption levels. SEM observations showed about the same particle size and morphology before and after ARS sorption. The TGA data showed the formation of CaO after Cal was heated, and CaO converted back into calcite after being in contact with water or ARS solution for 24 h and then being air-dried. Thus, the high ARS removal could be due to CaO produced after Cal being heated. The findings from this research proved that there is great potential in the use of calcite, a low-cost and readily available Earth material, after heat treatment for the removal of contaminants from water.