Abstract Transition metal carbides find widespread use throughout industry due to their high strength and resilience under extreme conditions. However, they remain largely limited to compounds formed from the early d‐block elements, since the mid‐to‐late transition metals do not form thermodynamically stable carbides. We report here the high‐pressure bulk synthesis of large single crystals of a novel metastable manganese carbide compound, MnC x ( P 6 3 /mmc ), which adopts the anti‐NiAs‐type structure with significant substoichiometry at the carbon sites. We demonstrate how synthesis pressure modulates the carbon loading, with ~40 % occupancy being achieved at 9.9 GPa.