Fusion Growth and Extraordinary Distortion of Ultrasmall Metal Oxide Nanoparticles

Ultrasmall metal oxide nanoparticles (<5 nm) potentially have new properties, different from conventional nanoparticles. The precise size control of ultrasmall nanoparticles remains difficult for metal oxide. In this study, the size of CeO2 nanoparticles was precisely controlled (1.3–9.4 nm) using a continuous-flow hydrothermal reactor, and the atomic distortion that occurs in ultrasmall metal oxides was explored for CeO2. The crystalline nanoparticles grow rapidly like droplets via coalescence, although they reach a critical particle size (∼3 to 4 nm), beyond which they grow slowly and change shape through ripening. In the initial growth stage, the ultrasmall nanoparticles exhibit disordered atomic configurations, including stacking faults. In ultrasmall CeO2 nanoparticles (<3 to 4 nm), unusual electron localization occurs on Ce 4f orbitals (Ce3+) as a result of O disordering, regardless of O vacancy concentration. This behavior differs from ordinary electron localization caused by the presence of O vacancies. The ultrasmall metal oxides have extraordinary distortion states, making them promising for use in nanotechnology applications. Furthermore, the proposed synthesis method can be applied to various other metal oxides and allows exploration of their properties.