Nano-Patterned Pt-Based Metallic Glass Electrocatalysts with In-Situ Copper Oxide Foam for Enhanced Hydrogen Evolution

Hydrogen is a promising energy carrier for replacing fossil fuels, and hydrogen production via hydrogen evolution reaction (HER) is an environmentally friendly option if electrocatalysts with low overpotentials and long-term stability are used. In this work, the electrocatalytic performance of Pt₅₇. ₅₂ₔ_₁₄. ₇Ni₅. ₃P₂₂. ₅ bulk metallic glass (BMG) with flat, micro-patterned, and nano-patterned surfaces for HER in 0. 5 M H2SO4 is studied. The nano-patterned Pt-BMG demonstrates outstanding long-term stability and self-improving behavior with a final overpotential of 150 mV and a Tafel slope of 42 mV dec^-1 after 1000 linear sweep voltammetry (LSV) cycles, which is respectively 42% and 37% lower than in the first LSV cycle. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) indicate the formation of a layer of CuO/Cu2O foam deposited on top of the nano-patterned surface during the stability test of 1000 LSV cycles. A three-step process is proposed to explain the formation of CuxO foam via dynamic hydrogen bubble templating (DHBT) electrodeposition from Cu dissolution of the Pt-BMG without using copper salt. This work provides a method to create CuxO foams that could be used for various applications. Moreover, nano-patterned BMGs with DHBT deposition offer a feasible strategy to synthesize metal or metal-oxide foams.