Unveiling the Mechanism in Nickel Loss During the Neutralization of Pregnant Acid Leach Solution by Various Alkaline Chemicals Using Electron Imaging, X-Ray Diffraction, and Electron Energy Loss Spectroscopy Analyses

Removal of iron and aluminum from nickel-bearing pregnant leach solution is imperative prior to recovering nickel. However, the mechanisms into the loss of both nickel and cobalt in precipitate products during the neutralization process remained unclear and debatable. In this study, the precipitation ratios of nickel, as well as other valuable metals in iron precipitate products, were investigated by examining bulk and surface properties of iron precipitates using X-ray diffraction, infrared spectroscopy, scanning electron microscopy, and electron energy loss spectroscopy. Amorphous ferrihydrite was identified as the major phase for iron precipitates. Over 99% precipitation ratio for iron and aluminum was achieved at pH 3. The loss of nickel in iron precipitates was strongly dependent on solution pHs, and the losses of nickel were found to be 3%, 8%, and 28% at pHs of 3, 4, and 5, respectively. The type of alkaline chemicals impacted the mineralogical composition of iron precipitate products and loss of valuable metals but had a minor impact on iron precipitation ratio. This work revealed three major mechanisms for the loss of nickel and cobalt during iron precipitation process: (1) entrainment of nickel-bearing PLS in filtered products, (2) surface adsorption on iron precipitates, and (3) lattice incorporation of nickel in iron precipitates. Additionally, the result of desorption experiments by H+ and Na+ ions showed that approximately 55–85% of lost nickel was incorporated within the lattice structure of iron precipitates, while the degree of nickel incorporation depends on the type of neutralizing reagents, precipitation conditions, and washing media.