This article presents research on the influence of reduced graphene oxide on the mechanical properties of silicon carbide matrix composites sintered with the use of the Spark Plasma Sintering method. The produced sinters were subjected to a three-point bending test. An increase in flexural strength was observed, which reaches a maximum value of 503.8 MPa for SiC–2 wt.% rGO composite in comparison to 323 MPa for the reference SiC sample. The hardness of composites decreases with the increase in rGO content down to 1475 HV10, which is correlated with density results. Measured fracture toughness values are burdened with a high standard deviation due to the presence of rGO agglomerates. The KIC reaches values in the range of 3.22–3.82 MPa*m1/2. Three main mechanisms responsible for the increase in the fracture toughness of composites were identified: bridging, deflecting, and branching of cracks. Obtained results show that reduced graphene oxide can be used as a reinforcing phase to the SiC matrix, with an especially visible impact on flexural strength.
Broniszewski et al. (Mon,) studied this question.