Abstract The micro-arc oxidation of TC4 titanium alloy was carried out by adding LuCl 3 . The effect of LuCl 3 addition on the properties of the micro-arc oxidized coatings, and the rate of weight loss by erosion under simulated oil field conditions, were analysed. The results show that the increase of oxidation voltage after the addition of LuCl 3 makes the surface structure of the coatings denser. The coating is mainly composed of Rutile TiO 2 , Anatase TiO 2 , and a small amount of Lu 2 O 3 phase. The kinetic potential polarization curves showed that the addition of LuCl 3 can increase the corrosion potential and decrease the corrosion current density of TC4 titanium alloy, and at the same time reduce the rate of erosion weight loss of micro-arc oxidized coatings under simulated oilfield conditions. The overall performance of the coatings is best when the concentration of LuCl 3 is 0.3 g L −1 .