Biosynthesis of iron oxide nanoparticles using plant extracts and evaluation of their antibacterial activity

Abstract The biosynthesis of iron oxide nanoparticles has received increasing attention in the field of food nanotechnology because of their non-toxicity, high efficiency, high antibacterial power, and decontamination features. Therefore, biosynthesis of iron oxide nanoparticles (nFe) was prepared from the leaves of some vegetables, such as cabbage (C) and turnips (T), as well as moringa leaves (M). Alcoholic extracts of these nanoparticles were also tested on Staphylococcus aureus and Escherichia coli to evaluate their antibacterial activity. The results revealed that the particle sizes of the biosynthesis nanomaterials studied ranged from 12.99 to 22.72 nm, and the particles were spherical, irregular, and surrounded by black color. It also contains many functional groups and minerals. Iron nanoparticles modified with Moringa oleifera extract at a concentration of 200 ppm had the highest phenol content compared to other biosynthesis nanoparticles studied. TnFe and MnFe at 200 ppm had a maximum zone of inhibition of 25 mm and 24 mm against Staphylococcus aureus and Escherichia coli , respectively. While the minimum inhibition zone of 8.0 mm was observed at 25 ppm for nFe against Escherichia coli . Therefore, it is recommended to use these extracts of biosynthesis iron oxide nanoparticles as antibacterial agents for stored foods.