This paper presents the experimental results of a study evaluating the mechanical and fatigue performance of welded Fe-Mn-Si SMA. For the experimental study, welded and welded-and-heat-treated Fe-Mn-Si SMA specimens were fabricated, and fatigue tests were performed at various stress amplitudes. In addition, direct tensile tests and recovery stress tests were also performed to evaluate the material properties of Fe-Mn-Si SMAs. The elastic modulus, yield strength, and tensile strength of the welded specimens were reduced by 35.4%, 12.1%, and 8.6%, respectively, compared to the values of the non-welded specimens. On the other hand, the elastic modulus, yield strength, and tensile strength of the welded-and-heat-treated Fe-Mn-Si SMA specimens were increased by 18.6%, 4.9%, and 1.3%, respectively, compared to the values of the welded specimens. Both welded and welded-and-heat-treated Fe-Mn-Si SMAs failed at lower cycles than the conventional Fe-Mn-Si SMAs at the same stress amplitude. High-cycle fatigue failure, characterized by cycles exceeding 10
Hong et al. (Fri,) studied this question.