This study focuses on investigating the strength recovery of fire-damaged fly ash concrete (FAC) with a low substitution rate of 10% through post-fire curing. The chemical and microstructural changes were analyzed using X-ray diffraction (XRD), derivative thermogravimetry (DTG), scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDS), and nitrogen adsorption. The findings indicate that the incorporation of fly ash slightly enhanced the strength after exposure to 400 °C; this was attributed to improved pozzolanic reactions, which were not observed at higher temperatures of 600 °C and 800 °C. Moreover, a positive effect on the recovery of compressive strength was observed due to the pozzolanic reaction. However, due to the relatively low fly ash content, depletion occurred at a later age, resulting in the inability to inhibit microstructural damage caused by the production of portlandite, thereby weakening the compressive strength. Interestingly, fly ash influenced the morphology of calcium carbonate and calcium silicate hydrate crystals, which is potentially ascribed to the role of high aluminum content acting as a crystallization-guiding agent.
Mi et al. (Sat,) studied this question.