AISI 431 martensitic stainless steels (MSS) with 2.5 wt% Cu were fabricated via laser-directed energy deposition additive manufacturing followed by single-step tempering treatment. The influences of different tempering times at 600 °C on microstructure and mechanical properties of the as-deposited 431-2.5Cu MSS have been explored and analyzed. The as-deposited MSS specimen primarily consisted of lath martensite, austenite and M23C6 carbide. After the single-step tempering treatment at 600 °C, Cu-enriched (ԑ-Cu) nano-precipitates and reverse austenite can be formed and promoted by extending the tempering treatment. The microhardness, strength and elongation can be improved with increasing the tempering time up to 1.0 h, and subsequently reduced with the tempering time prolonging to 2.0 h. Compared to 431 MSS that requires a multiple-step heat treatment for excellent performance, the 431-2.5Cu MSS specimen presented superior tensile properties after single-step tempering at 600 °C for 1.0 h in the present work. The ultimate tensile strength (UTS), yield strength (YS) and elongation (EL) of one-hour tempered MSS were 1611 MPa, 1334 MPa and 16.3%, respectively. This study provides a quantitative theoretical reference and experimental basis for realizing short-process fabrication of the Cu-bearing MSS with high strength and ductility.
Zhao et al. (Sat,) studied this question.