High-Entropy and Component Stoichiometry Tuning Strategies Boost the Sodium-Ion Storage Performance of Cobalt-Free Prussian Blue Analogues Cathode Materials

Prussian blue analogs (PBAs) are appealing cathode materials for sodium-ion batteries because of their low material cost, facile synthesis methods, rigid open framework, and high theoretical capacity. However, the poor electrical conductivity, unavoidable presence of Fe(CN)6 vacancies and crystalline water within the framework, and phase transition during charge–discharge result in inferior electrochemical performance, particularly in terms of rate capability and cycling stability. Here, cobalt-free PBAs are synthesized using a facile and economic co-precipitation method at room temperature, and their sodium-ion storage performance is boosted due to the reduced crystalline water content and improved electrical conductivity via the high-entropy and component stoichiometry tuning strategies, leading to enhanced initial Coulombic efficiency (ICE), specific capacity, cycling stability, and rate capability. The optimized HE-HCF of Fe0.60Mn0.10-hexacyanoferrate (referred to as Fe0.60Mn0.10-HCF), with the chemical formula Na1.156Fe0.599Mn0.095Ni0.092Cu0.109Zn0.105 Fe(CN)60.724·3.11H2O, displays the most appealing electrochemical performance of an ICE of 100%, a specific capacity of around 115 and 90 mAh·g−1 at 0.1 and 1.0 A·g−1, with 66.7% capacity retention observed after 1000 cycles and around 61.4% capacity retention with a 40-fold increase in specific current. We expect that our findings could provide reference strategies for the design of SIB cathode materials with superior electrochemical performance.