Effect of Trace Rare Earth Element Cerium (Ce) on Microstructure and Mechanical Properties of High Strength Marine Engineering Steel

In this paper, FH460 special steel with rare earth element cerium (Ce) was selected, and the control group without Ce was set up. By changing the content of Ce, the microstructure, phase transition point, and mechanical properties of the test steel were observed to study the effect of trace rare earth element Ce on the microstructure and mechanical properties of high-strength marine engineering steel. The morphology and energy spectrum of inclusions in three kinds of test steels were observed by SEM, and the morphological changes in inclusions in FH460 high-strength marine engineering steel after adding Ce were investigated. The fracture morphology and energy spectrum analysis were carried out by combining the tensile test at room temperature and the gradient low temperature impact toughness test, and the effect of trace Ce on the mechanical properties of the test steel was comprehensively analyzed. The results show that the addition of Ce changes the phase transformation temperature of Ac1 and Ac3, and refines the original microstructure of the test steel. SEM observation showed that the addition of Ce changed the long strip MnS and polygonal irregular Al2O3 inclusions into ellipsoids, which reduced the size of inclusions. The gradient low temperature impact test shows that with the decrease in temperature, the fracture dimple depth of the three test sheets of steel decreases, and the Ce-containing test steel forms a deep dimple centered on rare earth inclusions, which hinders the crack propagation and significantly improves the low temperature impact toughness of the test steel.