Comparative Analysis of Mechanical Properties and Microstructure of 7B52 Aluminum Alloy Laser-MIG Hybrid Welding and MIG Welding Joints

Laser-MIG hybrid welding and MIG welding were carried out on 7B52 aluminum alloy, and the microstructure and mechanical properties of the joints were compared and analyzed. The results show that the average grain sizes of laser-MIG hybrid welding, MIG welding, and the laser weld zone are 18.38 μm, 24.16 μm, and 15.96 μm, respectively. The width of the HAZ of the laser zone is lower than that of the laser-MIG hybrid welding zone and MIG welding zone. The hardness is higher than that of the hybrid welding zone and MIG welding zone. The tensile strength of each laser-MIG hybrid welding joint zone is better than that of the MIG welding zone. The tensile strength of the laser zone is the worst. When stress ratio R = 0.1 and fatigue cycle Nf = 106, the fatigue strength of the laminated zone of the laser-MIG hybrid welding joint is better than that of the MIG welding joint, and the welding defect is the leading cause of fatigue cracks.