A three-dimensional stochastic aggregate model of concrete was established using the Monte Carlo method, and a numerical simulation of chloride ion diffusion at the microscopic level was conducted. The study investigated the migration behaviour of chloride ions in concrete regarding mixing proportions and temperature. The results showed that compared to the simulation results at an ambient temperature of 20 ℃, the chloride ion diffusion coefficient increased by 31 % and 70.5 % for concrete at 25 ℃ and 30 ℃ at 28 days, respectively. The chloride ion penetration depth increased by 17.3 % and 34.9 % for concrete at 25 ℃ and 30 ℃, respectively. With a slag content of 10.4 %, 20.8 %, and 27.1 %, the chloride ion diffusion coefficient at 28 days decreased by 1.4 %, 2.7 %, and 4.1 %, respectively. With a fly ash content of 8.3 %, 16.7 %, and 25 %, the chloride ion diffusion coefficient at 28 days decreased by 2.1 %, 5.4 %, and 9.2 %, respectively. Both slag and fly ash can reduce the chloride ion diffusion coefficient in concrete, with fly ash showing better effectiveness than slag. A water-to-binder ratio of 0.4, combined with 27.1 % slag and 25 % fly ash as cement replacements, can effectively improve the resistance of concrete to chloride ion attack. The micro-scale finite element model of concrete, developed through Monte Carlo simulation, offers enhanced visualization of chloride ion penetration processes under varying mix proportions and temperature conditions.
Wen et al. (Sun,) studied this question.