This study evaluated a biomimetic filler strategy for two-step universal dental adhesives by integrating amine-functionalized mesoporous silica nanoparticles (MSNs) loaded with polyacrylic acid-stabilized amorphous calcium phosphate (PA–ACP) into the primer phase. MSNs were synthesized and characterized by FTIR, N2 sorption (BET), and HRTEM to confirm structural integrity and effective PA–ACP loading. Two commercial adhesives (G2 Bond and OptiBond eXTRa) were modified by incorporating different volumes fractions (10, 15, 20 vol%) of PA–ACP/MSN. Wettability (contact angle), microtensile bond strength (μTBS), and cytotoxicity (indirect MTT assay using human periodontal ligament fibroblasts, HPLFs) were assessed. The results demonstrated that incorporating up to 15 vol% PA–ACP/MSN maintained favorable wettability and bond strength, comparable to those of the unmodified controls. At 20 vol%, significant increases in contact angles and reductions in bond strength indicated impaired primer infiltration. Cytotoxicity testing confirmed high fibroblast viability (>70%) across all tested concentrations, verifying the biocompatibility of PA–ACP/MSN-filled primers. This work confirms the feasibility of a biomimetic adhesive design using PA–ACP/MSN in the primer phase without compromising immediate wettability and immediate μTBS up to 15 vol%. Remineralization is a potential capability that requires verification in future studies.
Alnakib et al. (Tue,) studied this question.