Coal gasification slag (CGS), an industrial solid waste produced during high-temperature (1200–1600 °C) coal gasification, was utilized as the primary raw material, combined with minor additions of coal gangue and calcium oxide, to synthesize ceramsite filter via high-temperature sintering (900–1160 °C) for phosphorus-containing wastewater treatment. The resulting ceramsite was evaluated for compressive strength, apparent porosity, water absorption, mineral phase composition, hydrolysis properties, and phosphorus removal performance. Experimental results revealed that increasing sintering temperature and calcium oxide content shifted the dominant crystalline phases from anorthite and hematite to gehlenite, anorthite, wollastonite, and esseneite, promoting the formation of porous structures. This transition increased apparent porosity while reducing compressive strength. Under optimal conditions (1130 °C, 20 wt.% CaO, 1 h sintering), the ceramsite (CM-20-1130) exhibited an apparent porosity of 43.12%, compressive strength of 3.88 MPa, apparent density of 1.084 g/cm3, and water absorption of 33.20%. The high porosity and abundant gehlenite and wollastonite phases endowed CM-20-1130 with enhanced hydrolysis capacity. Static phosphorus removal experiments demonstrated a maximum phosphorus removal capacity of 2.77 mg/g, driven by the release of calcium and hydroxide ions from gehlenite and wollastonite, which form calcium-phosphate precipitates on the ceramsite surface, enabling efficient phosphorus removal from simulated wastewater.
Li et al. (Mon,) studied this question.