This study fabricated six types of NiCr–Cr3C2 composite coatings using high-velocity oxygen fuel (HVOF) spraying and systematically evaluated their tribological behavior at 350 °C and 500 °C, along with their electrochemical corrosion performance in 3.5 wt.% NaCl solution. The objective was to elucidate how compositional design regulates the coatings’ microstructure, mechanical properties, and service performance. Results indicate that the 75NiCr–25Cr3C2 coating (C) formed a stable oxide film under both temperatures, exhibiting oxidation-dominated wear and the lowest friction coefficient and wear rate. When the temperature increased from 350 °C to 500 °C, the wear rates of coatings C, B, E, and F decreased significantly. Notably, coatings E and F, which contained CoCrFeNiMo high-entropy alloy, showed more than a 50% reduction in wear rate, demonstrating the contribution of the high-entropy phase to high-temperature wear resistance. At 350 °C, coatings B, D, E, and F experienced primarily abrasive wear; at 500 °C, however, E and F shifted to oxidative wear as the dominant mechanism, leading to a marked improvement in wear resistance. Electrochemical measurements revealed that coating E exhibited the best corrosion resistance, while the NiCr coating (A) performed the worst. The findings highlight that optimizing Cr3C2 content and incorporating high-entropy alloy elements can synergistically enhance both high-temperature tribological properties and corrosion resistance.
Zhang et al. (Wed,) studied this question.