The addition of Cu or La plays an important role in microstructure and property manipulation of 4xxx series Al-Si alloys. However, the effects of Cu-La hybrid modification on the microstructure and properties of Al-5Si alloys and welding performance remain unclear. In this paper, the influence of Cu-La addition on the strength and elongation of one commercial Al-5Si alloy and the welding joint characterization are investigated. The results show that the addition of Cu-La can refine α-(Al) and Fe-rich phase and improve the fluidity. Meanwhile, the elongation can be improved by Cu-La microalloying, which is beneficial for the manufacturing filler wire. The uniform distribution of Cu in the alloy but not segregation at grain boundaries due to La addition is the key factor to adjust the mechanical properties. Moreover, the filler materials were used to conduct metal inert gas welding on 6061 alloy. It reveals that, with Cu-La addition, the weld pool width increases and porosity defect decreases significantly. This is ascribed to Cu-La co-addition enhancing wettability and fluidity, which improves the welding performance. Our results offer an effective strategy for manufacturing and optimizing welding performance of welding wires.
Wu et al. (Fri,) studied this question.