Although TiO2 offers multiple advantages as an anode material for Na-ion batteries, achieving both elevated specific capacity and durable cycling stability remains a major hurdle for practical applications. This work demonstrates the outstanding Na-ion storage capability of TiO2 nanosheet anodes when employed in an ether-based electrolyte system (diglyme/NaPF6). The TiO2 anode achieved a superior specific capacity (214 mAh g-1 @ 25 mA g-1), demonstrated excellent rate capability (135 mAh g-1 @ 1 A g-1), retained 67% of its capacity after 6000 cycles, maintained nearly 100% Coulombic efficiency, and a pronounced pseudocapacitive contribution (∼59%), substantially outperforming the conventional carbonate-based electrolyte (EC-EMC/NaPF6), which showed only 18% pseudocapacitance. Interfacial analysis using ATR-FTIR and XPS verified the development of polyether-derived solid electrolyte interphase (SEI) upon charge-discharge cycling in a diglyme/NaPF6 solution. The superior Na-ion storing behavior is credited to superfast and pseudocapacitive (1.29 × 10-12 cm2/s) Na-ion diffusion through a SEI composed of polyether, in contrast to the slower diffusion observed with the polycarbonate-based counterpart (7.54 × 10-14 cm2/s). Furthermore, a full sodium-ion cell comprising a NaV3O8 cathode, nanosheet TiO2 anode, and 1 M diglyme/NaPF6 solution electrolyte demonstrated outstanding performance, delivering 67 mAh g-1 @ 1 A g-1 after 400 cycles, with 161 Wh kg-1 energy density. These findings underscore the critical role of the electrode-electrolyte interface in enhancing the pseudocapacitive Na-ion storage in TiO2-based anodes.
Maça et al. (Tue,) studied this question.